Products
Primary sealing
Hot applied primary sealant based on polyisobutylene. Developed specifically for application to aluminum spacer frame used later in the production of insulating glass units and optimally combined with secondary sealant, has good adhesion to glass, aluminum, zinc, steel.
Secondary sealing
The sealant is a two-component elastic mass used in the production of insulating glass units. The main functions of the secondary sealant are:
Provision of secondary protection by preventing moisture from penetrating into the insulating glass unit
Compensation for external loads and ensure the rigidity and integrity of the structure
Compensation for external loads and ensure the rigidity and integrity of the structure
Molecular sieve is a mixture of synthetic zeolite, substances with very low gas desorption capacity and high water adsorption capacity.
Main Functions:
Molecular sieve is a mixture of synthetic zeolite, substances with very low gas desorption capacity and high water adsorption capacity.
Absorption of moisture that penetrates through the side seams into the insulating glass unit during operation
The primary frame of the insulating glass unit, which maintains a certain distance between the panes of glass
Container for molecular sieve
Container for molecular sieve
Main Functions:
Molecular sieve
Spacer frame
Butyl
Primary sealing
Brand - PIB 996
Characteristic
Appearance
Density
Vapor
penetration
rate
Gas permeability
Condensate formation
Application
rate
Heating time
Packing
Resistance
Storage
Certificates
Appearance
Density
Vapor
penetration
rate
Gas permeability
Condensate formation
Application
rate
Heating time
Packing
Resistance
Storage
Certificates
Polyisobutylene based sealant with moisture vapor barrier for insulating glass units
Glossy black mass
1,12 g/cm3-1,25 g/cm3
0,02±0,3 gr H2O/(m2·24h·2mm) acc.EN1279:4
1,31±0,20 10-3 g/(m2·hour) acc. EN 1279:2002 5/3/2-EN 1279:3
Condensate <0.1 mg/ 10 mg Ұ-testing at 90℃/168 hrs
10-100 mt/min intermediate speed
20 min at 20℃ to 160℃ and 4 kW heat power
7 kg 185 mm diameter cylinders
50 full consecutive weeks of testing in the chamber at 60℃
Guaranteed shelf life of 24 months in original packaging, in a dry room at a temperature of +10℃ to +30℃
Certified by Rosenheim Institute (Germany) in accordance with EN 1279 NEDEX is certified by TÜV SÜD (Germany) in accordance with ISO 9001-2000.
Glossy black mass
1,12 g/cm3-1,25 g/cm3
0,02±0,3 gr H2O/(m2·24h·2mm) acc.EN1279:4
1,31±0,20 10-3 g/(m2·hour) acc. EN 1279:2002 5/3/2-EN 1279:3
Condensate <0.1 mg/ 10 mg Ұ-testing at 90℃/168 hrs
10-100 mt/min intermediate speed
20 min at 20℃ to 160℃ and 4 kW heat power
7 kg 185 mm diameter cylinders
50 full consecutive weeks of testing in the chamber at 60℃
Guaranteed shelf life of 24 months in original packaging, in a dry room at a temperature of +10℃ to +30℃
Certified by Rosenheim Institute (Germany) in accordance with EN 1279 NEDEX is certified by TÜV SÜD (Germany) in accordance with ISO 9001-2000.
Butyl
Primary sealing
Brand - PIB 996
Characteristic
Polyisobutylene based sealant with moisture vapor barrier for insulating glass units
Appearance
Glossy black mass
Density
1,12 g/cm3-1,25 g/cm3
Vapor penetration rate
0,02±0,3 gr H2O/(m2·24h·2mm) acc.EN1279:4
Gas permeability
1,31±0,20 10-3 g/(m2·hour) acc. EN 1279:2002 5/3/2-EN 1279:3
Condensate formation
Condensate <0.1 mg/ 10 mg Ұ-testing at 90℃/168 hrs
Application rate
10-100 mt/min intermediate speed
Heating time
20 min at 20℃ to 160℃ and 4 kW heat power
Packing
7 kg 185 mm diameter cylinders
Resistance
50 full consecutive weeks of testing in the chamber at 60℃
Storage
Guaranteed shelf life of 24 months in original packaging, in a dry room at a temperature of +10℃ to +30℃
Certificates
Certified by Rosenheim Institute (Germany) in accordance with EN 1279 NEDEX is certified by TÜV SÜD (Germany) in accordance with ISO 9001-2000.
Polyisobutylene based sealant with moisture vapor barrier for insulating glass units
Appearance
Glossy black mass
Density
1,12 g/cm3-1,25 g/cm3
Vapor penetration rate
0,02±0,3 gr H2O/(m2·24h·2mm) acc.EN1279:4
Gas permeability
1,31±0,20 10-3 g/(m2·hour) acc. EN 1279:2002 5/3/2-EN 1279:3
Condensate formation
Condensate <0.1 mg/ 10 mg Ұ-testing at 90℃/168 hrs
Application rate
10-100 mt/min intermediate speed
Heating time
20 min at 20℃ to 160℃ and 4 kW heat power
Packing
7 kg 185 mm diameter cylinders
Resistance
50 full consecutive weeks of testing in the chamber at 60℃
Storage
Guaranteed shelf life of 24 months in original packaging, in a dry room at a temperature of +10℃ to +30℃
Certificates
Certified by Rosenheim Institute (Germany) in accordance with EN 1279 NEDEX is certified by TÜV SÜD (Germany) in accordance with ISO 9001-2000.
Products - two-component polysulfide sealant for manual assembly of insulating glass units
Sealant for manual assembly
Brands: ARCOL, ALPHA Q, STARK CHEMIE, SOLO MIX
Solidification (Polymerization)
Primary setting (Viability)
Hardness
Packaging
Adhesion
Thixotropy (bench test)
Primary setting (Viability)
Hardness
Packaging
Adhesion
Thixotropy (bench test)
Solidification (Polymerization)
Primary setting (Viability)
Hardness
Packaging
Adhesion
Thixotropy (bench test)
Primary setting (Viability)
Hardness
Packaging
Adhesion
Thixotropy (bench test)
Products - two-component polysulfide sealant for automated assembly line for insulating glass units
Brands: PS998, Stark Chemie
Storage
Guaranteed shelf life 6 months in original packaging, in a dry room at 10℃ to 30℃. Avoid direct sunlight, rain and snow. Do not use at a temperature below 12℃
Certificates
Guaranteed shelf life 6 months in original packaging, in a dry room at 10℃ to 30℃. Avoid direct sunlight, rain and snow. Do not use at a temperature below 12℃
Certificates
- Industrial Certificate No. 105 1 00016
- Certificate of Conformity No. KZ.7500937.01.01.02386
- Certificate of Origin No. KZ 3 105 00211
Appearance
Density
Dynamic
viscosity
Ratio of
components
Density
Dynamic
viscosity
Ratio of
components
Appearance
Density
Dynamic
viscosity
Ratio of components
Density
Dynamic
viscosity
Ratio of components
Component A-beige (homogeneous material)
Component B-black (homogeneous material)
Component А-1.8-1.9 g/cm3
Component В-1.5-1.55 g/cm3
Component A-1000±100
Component B-100±10
by weight A:B-10:1
Component B-black (homogeneous material)
Component А-1.8-1.9 g/cm3
Component В-1.5-1.55 g/cm3
Component A-1000±100
Component B-100±10
by weight A:B-10:1
Cold setting (polymerization time) 40-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
20-25 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
SHOR A>48 after 24 hours at 23℃
Component A-30 kg; 4.5 kg; 27 kg
Component B-3 kg; 0.45 kg; 2.7 kg
More than 10 min at 0.3 mPa (H-test with 7 kg reinforcement) less than 1 mm for 3 mm thickness.
less than 1 mm for 3 mm thickness.
20-25 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
SHOR A>48 after 24 hours at 23℃
Component A-30 kg; 4.5 kg; 27 kg
Component B-3 kg; 0.45 kg; 2.7 kg
More than 10 min at 0.3 mPa (H-test with 7 kg reinforcement) less than 1 mm for 3 mm thickness.
less than 1 mm for 3 mm thickness.
Component A-beige (homogeneous material)
Component B-black (homogeneous material)
Component А-1.87-1.9 g/cm3
Component В-1.55-1.6 g/cm3
Component A-1200±100
Component B-100±10
by volume A:B-10:1
Component B-black (homogeneous material)
Component А-1.87-1.9 g/cm3
Component В-1.55-1.6 g/cm3
Component A-1200±100
Component B-100±10
by volume A:B-10:1
Cold setting (polymerization time) 80-120 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
45-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
SHOR A>45 after 24 hours at 23℃
Component A-355 kg; (190 L);
Component B-30 kg; (19 L);
more than 10 min at 0.3 mPa (H-test with 7 kg reinforcement)
less than 1 mm for 3 mm thickness
45-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
SHOR A>45 after 24 hours at 23℃
Component A-355 kg; (190 L);
Component B-30 kg; (19 L);
more than 10 min at 0.3 mPa (H-test with 7 kg reinforcement)
less than 1 mm for 3 mm thickness
Products - two-component polysulfide sealant for manual assembly of insulating glass units
Sealant for manual assembly
Brand: ARCOL, ALPHA Q, STARK CHEMIE, SOLO MIX
Products - two-component polysulfide sealant for automated assembly line for insulating glass units
Brand: PS998, Stark Chemie
Storage
Guaranteed shelf life 6 months in original packaging, in a dry room at 10℃ to 30℃. Avoid direct sunlight, rain and snow. Do not use at a temperature below 12℃
Certificates
Guaranteed shelf life 6 months in original packaging, in a dry room at 10℃ to 30℃. Avoid direct sunlight, rain and snow. Do not use at a temperature below 12℃
Certificates
- Industrial Certificate No. 105 1 00016
- Certificate of Conformity No. KZ.7500937.01.01.02386
- Certificate of Origin No. KZ 3 105 00211
Appearance
Component A-beige (homogeneous material)
Component B-black (homogeneous material)
Density
Component А-1.8-1.9 g/cm3
Component В-1.5-1.55 g/cm3
Dynamic viscosity
Component A-1000±100
Component B-100±10
Ratio of components
by weight A:B-10:1
Component A-beige (homogeneous material)
Component B-black (homogeneous material)
Density
Component А-1.8-1.9 g/cm3
Component В-1.5-1.55 g/cm3
Dynamic viscosity
Component A-1000±100
Component B-100±10
Ratio of components
by weight A:B-10:1
Solidification (Polymerization)
Cold setting (polymerization time) 40-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Primary setting (Viability)
20-25 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Hardness
SHOR A>48 after 24 hours at 23℃
Packaging
Component A-30 kg; 4.5 kg; 27 kg
Component B-3 kg; 0.45 kg; 2.7 kg
Adhesion
More than 10 min at 0.3 mPa (H-test with 7 kg reinforcement) less than 1 mm for 3 mm thickness.
Thixotropy (bench test)
less than 1 mm for 3 mm thickness.
Cold setting (polymerization time) 40-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Primary setting (Viability)
20-25 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Hardness
SHOR A>48 after 24 hours at 23℃
Packaging
Component A-30 kg; 4.5 kg; 27 kg
Component B-3 kg; 0.45 kg; 2.7 kg
Adhesion
More than 10 min at 0.3 mPa (H-test with 7 kg reinforcement) less than 1 mm for 3 mm thickness.
Thixotropy (bench test)
less than 1 mm for 3 mm thickness.
Appearance
Component A-beige (homogeneous material)
Component B-black (homogeneous material)
Density
Component А-1.87-1.9 g/cm3
Component В-1.55-1.6 g/cm3
Dynamic viscosity
Component A-1200±100
Component B-100±10
Ratio of components
by volume A:B-10:1
Component A-beige (homogeneous material)
Component B-black (homogeneous material)
Density
Component А-1.87-1.9 g/cm3
Component В-1.55-1.6 g/cm3
Dynamic viscosity
Component A-1200±100
Component B-100±10
Ratio of components
by volume A:B-10:1
Solidification (Polymerization)
Cold setting (polymerization time) 80-120 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Primary setting (Viability)
45-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Hardness
SHOR A>45 after 24 hours at 23℃
Packaging
Component A-355 kg; (190 L);
Component B-30 kg; (19 L);
Adhesion
more than 10 min at 0.3 mPa (H-test with 7 kg reinforcement)
Thixotropy (bench test)
less than 1 mm for 3 mm thickness.
Cold setting (polymerization time) 80-120 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Primary setting (Viability)
45-50 min at 23℃ and 50% relative humidity. When the temperature decreases, the curing time increases, and when the temperature increases, it decreases.
Hardness
SHOR A>45 after 24 hours at 23℃
Packaging
Component A-355 kg; (190 L);
Component B-30 kg; (19 L);
Adhesion
more than 10 min at 0.3 mPa (H-test with 7 kg reinforcement)
Thixotropy (bench test)
less than 1 mm for 3 mm thickness.
Molecular sieve
For automated assembly line
Brand: NANOMOL
Granule size
Packaging
Delta-
T index
Gas
desorption
Water absorption rate
Storage
Packaging
Delta-
T index
Gas
desorption
Water absorption rate
Storage
1.0-2.0 for semi-automatic and manual
filling
5 kg; 25 kg
>35℃ for 50g molecular sieve (20℃) with 50g
water
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Within the first 24 hours less than 8% ( at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
filling
5 kg; 25 kg
>35℃ for 50g molecular sieve (20℃) with 50g
water
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Within the first 24 hours less than 8% ( at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
For manual assembly
Brand: MULTIMOL, NEOMOL
Granule size
Packaging
Delta-
T index
Gas
desorption
Water absorption rate
Storage
Packaging
Delta-
T index
Gas
desorption
Water absorption rate
Storage
0.5-0.9-for automatic filling
25 kg
>35℃ for 50g molecular sieve (20℃) with 50g water
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Within the first 24 hours less than 8% ( at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
25 kg
>35℃ for 50g molecular sieve (20℃) with 50g water
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Within the first 24 hours less than 8% ( at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
Molecular sieve
For automated assembly line
Brand: NANOMOL
Granule size
1.0−2.0 for semi-automatic and manual
filling
Packaging
5 kg; 25 kg
Delta-T index
>35℃ for 50g molecular sieve (20℃) with 50g
water
Gas desorption
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Water absorption rate
Within the first 24 hours less than 8% (at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Storage
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
1.0−2.0 for semi-automatic and manual
filling
Packaging
5 kg; 25 kg
Delta-T index
>35℃ for 50g molecular sieve (20℃) with 50g
water
Gas desorption
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Water absorption rate
Within the first 24 hours less than 8% (at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Storage
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
For manual assembly
Brand: MULTIMOL, NEOMOL
Granule size
0.5-0.9-for automatic filling
Packaging
25 kg
Delta-T index
>35℃ for 50g molecular sieve (20℃) with 50g water
Gas desorption
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Water absorption rate
Within the first 24 hours less than 8% ( at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Storage
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
0.5-0.9-for automatic filling
Packaging
25 kg
Delta-T index
>35℃ for 50g molecular sieve (20℃) with 50g water
Gas desorption
Less than 50 mL for 250 g molecular sieve in 30 min at 70℃ after 3 hours contact with air. Given in ml of gas at 23℃ and 1000 mbar
Water absorption rate
Within the first 24 hours less than 8% ( at 23℃ and 32% humidity), then more than 24%. Very low electrostatic load. High flow with automatic filling. High hardness of granules as a result of curing process.
Storage
Guaranteed shelf life 18 months in original packaging, in a dry room at a temperature between 0℃ and 30℃
Spacer frame
Aluminum Spacer frame
Plastic spacer frame is one of the latest developments in window technology. This frame has a lot of advantages, including the possibility of manufacturing the frame in the color of the main profile.
PVC frame
The spacer frame is a specialized aluminum profile of welded construction with perforations in two rows.
Spacer frame sized:
5.5 mm;
8,5 mm;
9,5 mm;
11,5 mm;
13,5 mm;
15,5 mm;
23,5 mm.
Spacer frame sized:
5.5 mm;
8,5 mm;
9,5 mm;
11,5 mm;
13,5 mm;
15,5 mm;
23,5 mm.